EN ISO 14343-A: W 19 9 LSI
DIN 8556 SG – X2 CrNi 19 9
AWS A-5.9: ER308LSI
Uncoated corrosion-resistant rods for TIG welding of austenitic chromium-nickel steels, typically containing 18% Cr and 8% Ni. The filler metal offers good general corrosion resistance. The low carbon content makes it particularly useful in applications where there is a risk of intergranular corrosion. The increased silicon content improves weldability, such as wetting ability. This filler metal is widely used in the chemical and food industries, as well as for welding pipelines, tubes, and boilers.
Welded material | AlSl 304, 304L, W. Nr: 1.4301; 1.4541; 1.4550 itp. |
Shielding gas (EN ISO 14175) | I1 |
Welding current | =(-) |
Certifications | TÜV DB CE |
Product | Diameter | Packaging | Catalog number |
T07W (WIG) | 1,0mm | 5kg | T08W.064 |
T07W (WIG) | 1,2mm | 5kg | T08W.065 |
T07W (WIG) | 1,6mm | 5kg | T08W.066 |
T07W (WIG) | 2,0mm | 5kg | T08W.067 |
T07W (WIG) | 2,4mm | 5kg | T08W.068 |
T07W (WIG) | 3,2mm | 5kg | T08W.069 |
T07W (WIG) | 4,0mm | 5kg | T08W.070 |